Spandex fiber is the abbreviation of polyurethane fiber. The trade names include Lycra (Lycra, the United States, the United Kingdom, the Netherlands, Canada, Brazil), neolon (neolon, Japan), dorlastan (dorlastan, Germany), etc. Firstly, it was successfully studied by German Bayer company in 1937, and American DuPont company began industrial production in 1959. At present, there are nearly 40 factories and seven lines of production, with a total annual output of about 100000 tons, and China's existing production capacity of about 10000 tons. Spandex is a kind of synthetic fiber, which contains more than 85 percent polyurethane.
Existují dva druhy spandexových vláken, jeden je mozaikový kopolymer aromatické diisokyanázy a polyesterového segmentu obsahujícího hydroxyl (dále jen polyester spandex) a druhý je mozaikový kopolymer aromatického diisokyanátu a polyetherový segment obsahující hydroxyl (dále jen polyether spandex). Spandexové vlákno, elastické polyolefinové vlákno a elastické kompozitní vlákno se souhrnně označují jako elastické vlákno.
Syntetické vlákno s vysokou tažností při přetržení (více než 400 procent), nízkým modulem a vysokou elasticitou. Čínský obchodní název víceblokového polyuretanového vlákna. Také známé jako elastické vlákno. Spandex má vysokou tažnost (500 procent 700 procent), nízký modul pružnosti (200 procent prodloužení, 0,04 0,12 g / Dan) a vysokou elasticitu (200 procent tažnost, 95 procent 99 procent). Kromě vysoké pevnosti jsou další fyzikální a mechanické vlastnosti velmi podobné přírodnímu latexovému hedvábí. Je odolnější vůči chemické degradaci než latexový drát, má střední tepelnou stabilitu a teplota měknutí je nad 200 stupňů. Většina barviv a apretačních činidel používaných pro syntetická a přírodní vlákna je také vhodná pro barvení a konečnou úpravu spandexu. Spandex je odolný proti potu, mořské vodě a odolný vůči různým chemickým čisticím prostředkům a většině opalovacích krémů. Dlouhodobé vystavení slunečnímu světlu nebo chlórovému bělidlu také vybledne, ale stupeň vyblednutí se velmi liší podle typu spandexu.
Spandex fiber has such high elasticity because its polymer chain is composed of low melting point and amorphous "soft" segments as the matrix and high melting point and crystalline "hard" segments embedded in it. Flexible chain segments form a certain network structure by certain cross{{0}}linking between molecular chains. Due to the small interaction force between molecular chains, they can stretch freely, resulting in large elongation. The molecular linkage force of rigid segment is relatively large, and the molecular chain will not elongate indefinitely, resulting in high resilience. Most of the cross sections of radon fiber filaments are dog bone shaped, and some filaments have smooth or serrated surfaces. The breaking strength is the lowest among all textile fibers, only 0.44 0.88cn/dtex (the strength of polyether type is higher than that of polyester type). The moisture absorption range is small, generally 0.3-1.2 percent (the moisture absorption rate of multifilament is slightly higher than that of monofilament). The heat resistance varies greatly depending on the variety. Most fibers are stored in the range of 90 150 degree for a short time, and the fibers will not be damaged. The safe ironing temperature is below 150 degree , which can be heated and wet washed. It has excellent dyeing performance and can be dyed into various colors. The dyes have strong affinity for fiber, can adapt to most kinds of dyes, and has good chemical resistance, resistance to most acid and alkali, chemicals, organic solvents, dry cleaners and bleaches, as well as resistance to sunlight and wind and snow, but not oxide, which is easy to turn yellow and reduce the strength of fiber.
Spandex se obecně nepoužívá samostatně, ale malé množství se přimíchává do látky. Tento druh vlákna má vlastnosti pryže i vlákna. Většina z nich se používá v jádrové předené přízi se spandexem jako jádrovou přízí, která se nazývá elastická jádrová předená příze. Hlavní charakteristiky této příze jsou následující: za prvé může získat dobrý pocit z ruky a vzhled a vnější vlákno složené z přírodních vláken má dobrou absorpci vlhkosti; Za druhé, pouze 1-10 procent spandexového vlákna může produkovat vysoce kvalitní elastickou přízi; Za třetí, kontrolní rozsah procenta elasticity je od 10 procent do 20 procent a různé hodnoty elasticity lze vybrat podle účelu produktu. Je snadné spřádat hedvábí 25 2500 denier různé tloušťky, takže se široce používá k výrobě elastických tkaných látek, jako jsou ponožková ústa, potahy na nábytek, lyžařské oblečení, sportovní oblečení, lékařské tkaniny, opasky, vybavení Quartermaster, elastické části letectví. oblečení atd. S tím, jak lidé kladou nové požadavky na tkaniny, jako je nízká hmotnost, pohodlný střih a měkká textura, roste také podíl spandexových tkanin s nízkým denierem v tkaninách ze syntetických vláken. Používá se také jako skaná příze tvořená kombinací spandexového nahého hedvábí a spandexu a dalších vláken. Používá se hlavně pro všechny druhy osnovních pletenin a útkových pletenin, tkané látky a elastické tkaniny.